Stratasys DM9895
Data source: University of Debrecen
Compression strength X-Y: 1.5 MPa
Compressive modulus X-Y: 86.0 MPa
Compressive modulus Z: 21.6 MPa
Shore A hardness: 84.5
Listings by Stratasys
Stratasys DM9885
Data source: University of Debrecen
Compressive modulus X-Y: 15.4 MPa
Compressive modulus Z: 7.3 MPa
Shore A hardness: 71.7
Stratasys DM8530
Data source: University of Debrecen
Tensile strength X: 24.0 MPa
Tensile strength Y: 27.3 MPa
Tensile strength Z: 23.8 MPa
Compression strength X-Y: 44.3 MPa
Compression strength Z: 36.4 MPa
Bending strength X: 36.6 MPa
Bending strength Y: 46.1 MPa
Bending strength Z: 34.2 MPa
Young modulus X: 1,356 MPa
Young modulus Y: 1,548.0 MPa
Young modulus Z: 1,825.0 MPa
Compressive modulus X-Y: 1,254.0 MPa
Compressive modulus Z: 1,030.0 MPa
Shore D hardness: 75.8
Stratasys DM8525
Data source: University of Debrecen
Tensile strength X: 32.4 MPa
Tensile strength Y: 35.4 MPa
Tensile strength Z: 31.1 MPa
Compression strength X-Y: 62.5 MPa
Compression strength Z: 54.1 MPa
Bending strength X: 53.0 MPa
Bending strength Y: 67.8 MPa
Bending strength Z: 45.2 MPa
Young modulus X: 1,768 MPa
Young modulus Y: 1,898.0 MPa
Young modulus Z: 2,153.0 MPa
Compressive modulus X-Y: 1,658.0 MPa
Compressive modulus Z: 1,437.0 MPa
Shore D hardness: 78.3
Stratasys DM8520
Data source: University of Debrecen
Tensile strength X: 37.5 MPa
Tensile strength Y: 41.6 MPa
Tensile strength Z: 34.5 MPa
Compression strength X-Y: 72.1 MPa
Compression strength Z: 68.5 MPa
Bending strength X: 65.4 MPa
Bending strength Y: 80.1 MPa
Bending strength Z: 60.9 MPa
Young modulus X: 2,006 MPa
Young modulus Y: 2,159.0 MPa
Young modulus Z: 2,446.0 MPa
Compressive modulus X-Y: 1,959.0 MPa
Compressive modulus Z: 1,766.0 MPa
Shore D hardness: 80.3
Stratasys DM8515
Data source: University of Debrecen
Tensile strength X: 40.7 MPa
Tensile strength Y: 44.3 MPa
Tensile strength Z: 36.5 MPa
Compression strength X-Y: 78.2 MPa
Compression strength Z: 76.7 MPa
Bending strength X: 70.4 MPa
Bending strength Y: 85.2 MPa
Bending strength Z: 72.5 MPa
Young modulus X: 2,123 MPa
Young modulus Y: 2,264.0 MPa
Young modulus Z: 2,604.0 MPa
Compressive modulus X-Y: 1,995.0 MPa
Compressive modulus Z: 1,947.0 MPa
Shore D hardness: 80.8
Stratasys DM8510
Data source: University of Debrecen
Tensile strength X: 38.5 MPa
Tensile strength Y: 45.2 MPa
Tensile strength Z: 37.5 MPa
Compression strength X-Y: 79.0 MPa
Compression strength Z: 77.8 MPa
Bending strength X: 73.4 MPa
Bending strength Y: 87.4 MPa
Bending strength Z: 77.2 MPa
Young modulus X: 2,022 MPa
Young modulus Y: 2,320.0 MPa
Young modulus Z: 2,709.0 MPa
Compressive modulus X-Y: 2,005.0 MPa
Compressive modulus Z: 1,982.0 MPa
Shore D hardness: 81.1
Stratasys DM8505
Data source: University of Debrecen
Tensile strength X: 40.0 MPa
Tensile strength Y: 45.1 MPa
Tensile strength Z: 39.1 MPa
Compression strength X-Y: 81.6 MPa
Compression strength Z: 79.0 MPa
Bending strength X: 76.2 MPa
Bending strength Y: 90.6 MPa
Bending strength Z: 86.0 MPa
Young modulus X: 2,078 MPa
Young modulus Y: 2,293.0 MPa
Young modulus Z: 2,686.0 MPa
Compressive modulus X-Y: 2,099.0 MPa
Compressive modulus Z: 2,061.0 MPa
Shore D hardness: 81.3
Stratasys Veroclear
Data source: University of Debrecen
Tensile strength X: 58.9 MPa
Tensile strength Y: 63.1 MPa
Tensile strength Z: 34.0 MPa
Compression strength X-Y: 94.7 MPa
Compression strength Z: 95.3 MPa
Bending strength X: 93.1 MPa
Bending strength Y: 95.9 MPa
Bending strength Z: 94.1 MPa
Young modulus X: 2,680 MPa
Young modulus Y: 2,512.0 MPa
Young modulus Z: 2,896.0 MPa
Compressive modulus X-Y: 2,317.0 MPa
Compressive modulus Z: 2,324.0 MPa
Shore D hardness: 82.6
Stratasys Verowhite Plus
Data source: University of Debrecen
Tensile strength X: 40.0 MPa
Tensile strength Y: 46.6 MPa
Tensile strength Z: 39.9 MPa
Compression strength X-Y: 81.0 MPa
Compression strength Z: 80.4 MPa
Bending strength X: 75.0 MPa
Bending strength Y: 92.2 MPa
Bending strength Z: 93.8 MPa
Young modulus X: 2,076 MPa
Young modulus Y: 2,358.0 MPa
Young modulus Z: 2,601.0 MPa
Compressive modulus X-Y: 2,040.0 MPa
Compressive modulus Z: 2,022.0 MPa
Shore D hardness: 81.5